Izitini ze-Silica (T-3)
Incazelo Silica Bricks
Isetshenziselwa ikakhulukazi izindonga zokuhlukanisa zegumbi le-carbonization kanye negumbi elivuthayo lamahhavini e-coke, ama-regenerator kanye nama-slag amagumbi omlilo okwenza insimbi avulekile, izithando zokucwiliswa, izinto eziphikisayo zezithando zomlilo ezincibilika ingilazi kanye neziko lomlilo le-ceramic, nezinye iziko. ama-vaults. Izingxenye ezithwala imithwalo. Ibuye isetshenziselwe ezingxenyeni ezithwala izinga lokushisa eliphezulu leziqhumane ezishisayo neziqongo zesithando somlilo esine-acidic esivulekile.
Ipharamitha yezitini ze-silica
INTO | YC-94K | YC-95B | YC-95A | YC-96B | YC-96A | |
---|---|---|---|---|---|---|
SiO2 % | ≥94 | ≥95 | ≥95 | ≥96 | ≥96 | |
Fe203 % | ≤1.5 | ≤1.2 | ≤1.2 | ≤1.0 | ≤0.8 | |
I-Refractoriness ℃ | ≥1710 | ≥1710 | ≥1710 | ≥1710 | ≥1710 | |
AP % | ≤24 | ≤22(24 | ≤22(24) | ≤22(24) | ≤22(24) | |
BD g/cm3 | ≤2.33 | ≤2.35 | ≤2.35 | ≤2.34 | ≤2.34 | |
I-MPa | ≥20KG | ≥30 | ≥30(25) | ≥30(25) | ≥30(25) | ≥30(25) |
≥35(30 | ≥35(30) | ≥35(30 | ≥35(30) | |||
I-RUL ℃ | ≥1630 | ≥1650 | ≥1660 | ≥1670 | ≥1680 |
Izitini zeSilica ze-Coke Oven
Ohhavini besimanje be-coke bayimishini emikhulu eshisayo eyakhiwe ngamashumi ezinkulungwane zamathani kanye nezinhlobo ezicishe zibe inkulungwane zezinto eziphikisayo zezitini, lapho izitini ze-silica zenza ama-60% kuya ku-70%. Ingxenye eyinhloko yezitini ze-silica zamahhavini e-coke i-tridymite, esetshenziselwa kakhulu ukwakha izindonga zokuvuselela i-oven ye-coke, ama-chute, amakamelo omlilo, amagumbi e-carbonization kanye neziqongo zesithando somlilo. Izitini ze-silica zamahhavini e-coke ikakhulukazi zinezici zokushisa okuphezulu okuthambisa ngaphansi komthwalo, ukuqhutshwa kokushisa okuphezulu, ukumelana nokushaqeka okuhle kokushisa, nokuzinza kwevolumu emazingeni okushisa aphezulu.
Izitini zeSilica Zokushisela Ngengilazi
Izitini ze-silica zokushisa ingilazi zisetshenziselwa ukwakha izingxenye ezishisa kakhulu zokushisa ingilazi. Banezici ezilandelayo:
ukumelana kwamakhemikhali
Ukuminyana kwevolumu ephansi
Akukho ukungcola engilazini
Umthamo uzinzile emazingeni okushisa aphezulu, futhi umzimba wesithando somlilo ngeke ushintshe ngenxa yokushintshashintsha kwezinga lokushisa.