Agbara-giga ati ki o wọ-sooro castable
Agbara-giga ati ki o wọ-sooro castable
Atọka orukọ ọja | Ga alumina simenti refractory castable | Kekere kalisiomu aluminate cementRefractory castable | ||||
Amo refractory castable | Ga aluminiomu refractory castable | |||||
Aluminiomu-40 | Aluminiomu-50 | Aluminiomu-55 | Aluminiomu-65 | Aluminiomu-70 | ||
Iwọn iwọn didun (110 ℃ ± 5 ℃ x24h)) | kg/m | Ọdun 1900 | 2100 | 2200 | 2300 | 2500 |
Gbigbe agbara compressive | Mpa | 20 | mẹta-le-logun | 20 | mẹta-le-logun | 40 |
Gbigbe agbara flexural | Mpa | 4 | 5 | 4 | 5 | 6 |
800 ℃ ga otutu péye agbara | % | 40 | 50 | 40 | 50 | 60 |
Iduroṣinṣin mọnamọna gbona | Oṣuwọn keji | 15 | 15 | 15 | 15 | 20 |
Laini yipada lẹhin sisun, tutu fun 3h, ko ju 1% ti iwọn otutu adanwo | ℃ | 1200 | 1250 | 1300 | 1350 | 1400 |
Refractory ìyí | ℃ | 1650 | Ọdun 1670 | 1700 | Ọdun 1730 | Ọdun 1770 |
AL203> | % | 40 | 50 | 55 | 65 | 75 |
Max patiku iwọn ti refractory akopọ | mm | Nigbati sisanra sisan jẹ ≤60mm, ≤5mm | ||||
Nigbati sisanra sisan jẹ 60-100, ≤10mm | ||||||
Nigbati sisanra sisan jẹ ≥100mm, |
Ohun elo ọja
Henan Xinyuan Refractory Co., Ltd. ti wa ni ibatan si Yuzhou Xinyuan Refractory Materials Co., Ltd. Ile-iṣẹ naa wa ni ipilẹ ile-iṣẹ ti o tobi julo ti China: Changzhuang Town, ariwa-oorun ti ilu Yuzhou. Ti a da ni Oṣu Keje 2002. O jẹ ile-iṣẹ iṣọpọ ti o n ṣepọ iwakusa bauxite, firing bauxite, iwadii imọ-ẹrọ refractory ati idagbasoke, iṣelọpọ refractory ati masonry kiln. Ile-iṣẹ ni bayi ni kiln eefin iwọn otutu giga 168m, 120m giga-qualithic-temperature tunnel kinl. a magnẹsia erogba biriki makirowefu adiro. bauxite sinterina shaft kiln 4. eauinped pẹlu diẹ ẹ sii ju 20pcs 315-1200 toonu ti titẹ laifọwọyi, diẹ sii ju awọn oṣiṣẹ 300, pẹlu awọn oṣiṣẹ imọ-ẹrọ 50 ati awọn oṣiṣẹ imọ-ẹrọ, ile-iṣẹ naa ni: ile-iṣẹ biriki ti o wuwo, ile-iṣẹ biriki ina refractory, ile-iṣẹ iṣelọpọ meterail refractory ti ko ni apẹrẹ, Lt le pese awọn ohun elo ti o ni agbara giga fun irin, smelting nonferrous, ile-iṣẹ aluminiomu, gilasi, agbara, awọn ohun elo ile, epo.