Corundum Castable
Umsebenzi weMveliso
Xa kuthelekiswa ne-alumina ephezulu enokuphoswa kunye ne-mullite castable, i-corundum castable inamandla aphezulu omatshini kunye nokumelana nokunxiba, kodwa ukuxhathisa ukothuka kwe-thermal akulunganga njenge-mullite castable. Ukongeza inani elithile le-mullite kwizinto eziluhlaza kunokuphucula ukuxhatshazwa kwe-thermal shock ye-corundum castable. I-Corundum castable inamandla aphezulu okucinezela kunye nokuzinza okuhle kwesakhiwo. Umthamo omkhulu, i-corundum castable casting lining inokumelana ne-slag corrosion, ukumelana nokunyamezela, ukumelana nokunxiba okuphezulu kunye nokuchasana okunamandla kumasuntswana aqinileyo, umgubo kunye nobushushu obuphezulu bokukhukuliseka kwegesi.
Iimveliso zeCorundum Castable
Ukusebenza / Inqaku lenqaku | ZJ-1 | ZJ-2 | ZJ-18A | ZJ-18HS | ZJ-18H | |
ukwakheka kweekhemikhali% | Al2O3 | ≥98 | ≥95 | ≥95 | ≥95 | z95 |
SiO2 | ≤0.2 | ≤0.5 | ≤0.2 | ≤0.4 | ≤0.4 | |
Ubushushu obuphezulu bokusebenza℃ | 1850 | 1800 | 1800 | 1800 | 1800 | |
Ubuninzi bokuxinana emva kokubhaka kwi-110 ℃ g/cm3 | ≥3.1 | ≥3.0 | ≥2.9 | ≥30 | ≥3.1 | |
1500 ℃x3h Umgca utshintsha emva kokutshisa% | -0.2 ~ 0.6 | -0.2 ~ 0.6 | -0.2 ~ 0.7 | 0.1~-0.3(1100℃) | ±0.5 | |
Amandla acinezelayo kunye ne-flexural Mpa | 110℃x24h | ≥ 20/z4 | ≥60/≥7 | ≥50/≥4 | ≥60/≥8 | ≥70/≥7 |
1100℃x3h | ≥50/ ≥6 | ≥70/≥8 | ≥70/≥9 | ≥80/≥10 | ||
1500℃x3h | ≥60/ ≥10 | ≥100/ ≥15 | ≥100/≥15 | ≥120/≥10 | ≥150/15 | |
Ubungakanani bobungakanani bamasuntswana mm | 5-6 | 5-6 | 5-6 | 3 | 5-6 | |
Ukusetyenziswa kwamanzi ekwakhiweni (umlinganiselo wobunzima) | 5-6.5 | 5-6.5 | 5-6 | 5-6 | 5-6 |