Corundum Castable
Mosebetsi oa Sehlahisoa
Ha ho bapisoa le alumina e phahameng e ka lahlehang le ea mullite castable, corundum castable e na le matla a holimo a mochine le ho hanyetsa ho apara, empa ho hanyetsa mocheso oa mocheso ha ho molemo joaloka mullite castable. Ho eketsa palo e itseng ea mullite ka thepa e tala ho ka ntlafatsa ho hanyetsa mocheso oa mocheso oa corundum castable. Corundum castable e na le matla a phahameng a khatello le botsitso bo botle ba sebopeho. Bokhoni bo boholo, lesela la corundum castable casting le na le khanyetso e ntle ea slag corrosion, ho hanyetsa ho kenella, ho hanyetsa ho roala ho phahameng le ho hanyetsa ka matla ho likaroloana tse tiileng, phofo le khoholeho ea mocheso o phahameng oa khase.
Lihlahisoa tsa Corundum Castable
Tshebetso / Ntho No | ZJ-1 | ZJ-2 | ZJ-18A | ZJ-18HS | ZJ-18H | |
khemikhale% | Al2O3 | ≥98 | ≥95 | ≥95 | ≥95 | z95 |
SiO2 | ≤0.2 | ≤0.5 | ≤0.2 | ≤0.4 | ≤0.4 | |
Mocheso o phahameng oa ho sebetsa℃ | 1850 | 1800 | 1800 | 1800 | 1800 | |
Boima ba bongata ka mor'a ho baka ho 110 ℃ g/cm3 | ≥3.1 | ≥3.0 | ≥2.9 | ≥30 | ≥3.1 | |
1500 ℃x3h Line ea fetoha ka mor'a ho chesa% | -0.2–0.6 | -0.2–0.6 | -0.2–0.7 | 0.1~-0.3(1100℃) | ±0.5 | |
Matla a hatellang le a fetofetohang Mpa | 110 ℃x24h | ≥ 20/z4 | ≥60/≥7 | ≥50/≥4 | ≥60/≥8 | ≥70/≥7 |
1100 ℃x3h | ≥50/ ≥6 | ≥70/≥8 | ≥70/≥9 | ≥80/≥10 | ||
1500 ℃x3h | ≥60/ ≥10 | ≥100/ ≥15 | ≥100/≥15 | ≥120/≥10 | ≥150/15 | |
Boholo ba karoloana mm | 5-6 | 5-6 | 5-6 | 3 | 5-6 | |
Tšebeliso ea metsi kaho (karolelano ea boima) | 5-6,5 | 5-6,5 | 5-6 | 5-6 | 5-6 |