Ugereranije na alumina yo hejuru hamwe na mullite castable, corundum castable ifite imbaraga za mashini kandi ikarwanya kwambara, ariko guhangana nubushyuhe bwumuriro ntabwo ari byiza nka mullite castable. Ongeramo umubare munini wa mullite mubikoresho fatizo birashobora kunoza ubushyuhe bwumuriro wa corundum castable. Corundum castable ifite imbaraga zo gukomeretsa kandi zihamye zubaka. Ubushobozi bunini, corundum castable casting lining ifite uburyo bwiza bwo kurwanya ruswa, kwihanganira kwangirika, kwangirika kwinshi no kurwanya imbaraga zikomeye, ifu nisuri yubushyuhe bwo hejuru.
Ibicuruzwa bya Corundum
Imikorere / Ingingo Oya | ZJ-1 | ZJ-2 | ZJ-18A | ZJ-18HS | ZJ-18H | |
ibigize imiti% | Al2O3 | ≥98 | ≥95 | ≥95 | ≥95 | z95 |
SiO2 | ≤0.2 | ≤0.5 | ≤0.2 | ≤0.4 | ≤0.4 | |
Ubushyuhe bukabije bwo gukora ℃ | 1850 | 1800 | 1800 | 1800 | 1800 | |
Ubwinshi bwinshi nyuma yo guteka kuri 110 ℃ g / cm3 | ≥3.1 | ≥3.0 | ≥2.9 | ≥30 | ≥3.1 | |
1500 ℃ x3h Umurongo uhinduka nyuma yo gutwika% | -0.2 ~ 0.6 | -0.2 ~ 0.6 | -0.2 ~ 0.7 | 0.1 ~ -0.3 (1100 ℃) | ± 0.5 | |
Imbaraga zo guhonyora no guhinduka Mpa | 110 ℃ x24h | ≥ 20 / z4 | ≥60 / ≥7 | ≥50 / ≥4 | ≥60 / ≥8 | ≥70 / ≥7 |
1100 ℃ x3h | ≥50 / ≥6 | ≥70 / ≥8 | ≥70 / ≥9 | ≥80 / ≥10 | ||
1500 ℃ x3h | ≥60 / ≥10 | ≥100 / ≥15 | ≥100 / ≥15 | ≥120 / ≥10 | ≥150 / 15 | |
Ingano nini ya mm | 5-6 | 5-6 | 5-6 | 3 | 5-6 | |
Gukoresha amazi yo kubaka % ratio igipimo cy'uburemere) | 5-6.5 | 5-6.5 | 5-6 | 5-6 | 5-6 |