Humilis Caementum Castables
PRODUCTS
Summus fortitudo et lapsum repugnans castable
Details of Andalusite Brick
Summus fortitudo et lapsum repugnans castable
| Product nomen index | Princeps alumina caementum refractorium castable | Humilis calcium aluminatum cementRefractory castable | ||||
| Lutum refractior castable | Altuminium refractorium castable | |||||
| aluminium-40 | aluminium-50 | aluminium-55 | aluminium-65 | aluminium-70 | ||
| Volumen densitatis（110℃±5℃x24h）＞ | kg/m | 1900 | 2100 | MMCC | 2300 | 2500 |
| Siccatio compressive vires | Mpa | 20 | viginti tres | 20 | viginti tres | 40 |
| Siccatio flexus vi | Mpa | 4 | 5 | 4 | 5 | 6 |
| DCCC℃ caliditas RELICTUM viribus | % | 40 | 50 | 40 | 50 | 60 |
| Scelerisque inpulsa stabilitas | Secundus-rate | 15 | 15 | 15 | 15 | 20 |
| Linea mutatur post combustionem, humectantis pro 3h, non plus quam 1% caliditatis experimentalis | ℃ | 1200 | 1250 | 1300 | 1350 | 1400 |
| Repugnantia gradus | ℃ | 1650 | 1670 | 1700 | 1730 | 1770 |
| AL203> | % | 40 | 50 | 55 | 65 | 75 |
| Max particula aggregati magnitudinem refractionis | mm | Cum effusio crassitudinis sit ≤60mm, ≤5mm | ||||
| Effusio crassitudinis 60-100, ≤10mm | ||||||
| Cum effusio ≥100mm est, | ||||||
Product Function
Fornax ferrosilicon est fornax industrialis electrica quae multum comedit et est species fornacis arcus demersae. Fornax ferrosilicon includit testam fornacem, fornax operculum, fornax oblinit, rete breve, systema refrigerationis aquae, systema fumi exhauriunt, systema pulvis remotionis, testudo electrode, pressionis electrodum emissio et ratio elevatio, ratio onerandi et exonerandi, moderatoris, combustionis per machinam, hydrau. systema, TRANSFIGURATOR Et varia instrumenta electrica, etc., usus materiae refractoriae etiam satis flagitat.
Anno 2006, officina nostra in Yuzhou, basis rudis materiae condita est. Aes bauxite subtiliter divisa est mixtura colloidalis ex aluminio hydroxidis et variis rationibus composita. Summus alumina bauxite in industria refractoria plerumque ad bauxite chalcitis cum Al₂O₃ combusto contentum maiorem quam 48% et humili contentus Fe₂O refert.