PRODUCTS
Alta alumina refractaria castable
Singula
Alta alumina castella refractaria late in structura et sustentatione laterum industrialium adhibetur. Communia princeps alumina castables includunt caementum castabile portlandi, calcium aluminatum caementum castabile, aqua vitreum castabile connexum, phosphatum castabile connexum et cetera. Continua innovatione generum productorum, qualitas castellalium alta alumina etiam paulatim aucta est, inclusa castella refractaria humilis, castella ultra humilem caementa et castellarum caementa gratuita.
Alta alumina refractaria castable
Product nomen / index | Princeps alumina caementum refractorium castable | Humilis calcium aluminatum cementRefractory castable | ||||
Lutum refractior castable | Altuminium refractorium castable | |||||
aluminium-40 | aluminium-50 | aluminium-55 | aluminium-65 | aluminium-70 | ||
Volumen densitatis(110℃±5℃x24h)> | kg/m | 1900 | 2100 | MMCC | 2300 | 2500 |
Siccatio compressive vires | Mpa | 20 | viginti tres | 20 | viginti tres | 40 |
Siccatio flexus vi | Mpa | 4 | 5 | 4 | 5 | 6 |
DCCC℃ caliditas RELICTUM viribus | % | 40 | 50 | 40 | 50 | 60 |
Scelerisque inpulsa stabilitas | Secundus-rate | 15 | 15 | 15 | 15 | 20 |
Linea mutatur post combustionem, humectantis pro 3h, non plus quam 1% caliditatis experimentalis | ℃ | 1200 | 1250 | 1300 | 1350 | 1400 |
Repugnantia gradus | ℃ | 1650 | 1670 | 1700 | 1730 | 1770 |
AL203> | % | 40 | 50 | 55 | 65 | 75 |
Max particula aggregati magnitudinem refractionis | mm | Cum effusio crassitudinis sit ≤60mm, ≤5mm | ||||
Effusio crassitudinis 60-100, ≤10mm | ||||||
Cum effusio ≥100mm est, |
Product Applicationem
alta alumina castella refractaria apta est fornacem calefaciendi, fornacem maceratam, caloris curationem fornacem et fornacem gyratorius; Varius summus temperatus ustor linimentorum, fistulae aquae fornacis calefaciens liniamenta involvens, partes expolitio instrumentorum extra fornacem ferro fusilem et altae temperaturae lapsum repugnant liniamenta reactoria catalyticae petrochemicae catalyticae; Liners sicut fornax furoris taphoe, cupola taphola, integralis pulveris sclopetorum pro praetractatione metalli calida, etc. Etiam magnas praefabricatas caudices fabricare et fornacem linamenta celeri constructione fabricare potest.