HANA
Kiʻekiʻe alumina refractory castable
Nā kikoʻī
Hoʻohana nui ʻia ka alumina refractory castable i ka masonry a me ka mālama ʻana i nā kiln ʻoihana. ʻO nā mea hoʻoheheʻe alumina kiʻekiʻe maʻamau, ʻo ia ka portland cement castable, calcium aluminate cement castable, wai aniani hoʻopaʻa ʻia castable, phosphate hoʻopaʻa castable a pēlā aku. Me ka hoʻomau mau ʻana o nā ʻano huahana, ua hoʻomaikaʻi maikaʻi ʻia ka maikaʻi o nā mea hoʻoheheʻe alumina kiʻekiʻe, e komo pū me nā mea hoʻoheheʻe haʻahaʻa haʻahaʻa, nā mea hoʻoheheʻe haʻahaʻa haʻahaʻa a me nā pahu kima ʻole.
Kiʻekiʻe alumina refractory castable
inoa huahana / kuhikuhi | Kiʻekiʻe alumina sima refractory castable | Haʻahaʻa calcium aluminate cementRefractory castable | ||||
Pālolo refractory castable | Kiʻekiʻe alumini refractory castable | |||||
Aluminum-40 | Aluminum-50 | Aluminum-55 | Aluminum-65 | Aluminum-70 | ||
Ka nui o ka leo (110℃±5℃x24h)> | kg/m | 1900 | 2100 | 2200 | 2300 | 2500 |
Ka ikaika compressive maloʻo | Mpa | 20 | iwakāluakūmākolu | 20 | iwakāluakūmākolu | 40 |
Ka ikaika wiliwili maloʻo | Mpa | 4 | 5 | 4 | 5 | 6 |
800 ℃ kiʻekiʻe wela koena ikaika | % | 40 | 50 | 40 | 50 | 60 |
Paʻa haʻalulu wela | Kalua-helu | 15 | 15 | 15 | 15 | 20 |
Hoʻololi ka laina ma hope o ka puhi ʻana, hoʻomaʻemaʻe ʻia no 3h, ʻaʻole ʻoi aku ma mua o 1% o ka mahana hoʻokolohua | ℃ | 1200 | 1250 | 1300 | 1350 | 1400 |
Degere refractory> | ℃ | 1650 | 1670 | 1700 | 1730 | 1770 |
AL203> | % | 40 | 50 | 55 | 65 | 75 |
ʻO ka nui o ka nui o ka ʻāpana refractory | mm | Ke ≤60mm ka mānoanoa ninini, ≤5mm | ||||
Ke 60-100 ka mānoanoa ninini, ≤10mm | ||||||
Ke ≥100mm ka mānoanoa ninini, |
Hoʻohana Huahana
ʻO ka alumina refractory castable kiʻekiʻe he kūpono no ka umu hoʻomehana, ka umu ahi, ka umu hoʻomaʻamaʻa wela a me ka rotary kiln; ʻO nā linings kuni wela kiʻekiʻe, nā ʻāpana hoʻoheheʻe wai i ka umu ahi, nā ʻāpana o nā mea hana hoʻomaʻemaʻe ma waho o ka umu kila hoʻoheheʻe ʻia a me nā linings kūʻokoʻa wela o ka petrochemical catalytic cracking reactors; ʻO nā laina laina e like me ka blast furnace taphole, cupola taphole, integral powder gun for hot metal pretreatment, etc. Hiki ke hoʻohana ʻia e hana i nā poloka prefabricated nui a me nā linings umu no ka hana wikiwiki.